乐泰 ECCOBOND F 123 is formulated for terminating single or multi-channel fiber optic connectors. 乐泰 ECCOBOND F 123 bonds offer resistance to water and weathering, gasses, petroleum products and other organic and inorganic compounds.

TYPICAL PROPERTIES OF UNCURED MATERIAL

Thixotropic Index 1.0

Viscosity @ 25 °C, cP:

After Mixing 4,000

Specific Gravity, mixed 1.2

Reactive solids contents, % 100

Pot Life , hours 4

Flash Point - See SDS

TYPICAL CURING PERFORMANCE

Cure Schedule

5 minutes @ 100°C

Alternative Cure Schedule

2 minutes @ 120°C or

1 minute @ 150°C

An additional post cure of 30 minutes @ 150oC is recommended when application temperatures higher than 150oC are anticipated.

For masses over 0.25grams, allow material to gel for 4 hours @ 25oC followed by 100oC for 5 hours

The above cure profiles are guideline recommendations. Cure conditions (time and temperature) may vary based on customers' experience and their application requirements, as well as customer curing equipment, oven loading and actual oven temperatures.

TYPICAL PROPERTIES OF CURED MATERIAL

Physical Properties

Coefficient of Thermal Expansion ppm/°C:

Below Tg 6.31×1001

Above Tg 2.03×1002

Glass Transition Temperature (Tg), °C 120

Hardness, Shore D 87

Refractive Index 1.56

Water Absorption, % 0.004

Spectral transmittance (6,000 to 9,000 Å), % 93

Electrical Properties

Dielectric Strength, volts/mil 400

乐泰eccobond F 123是终止单或多通道光纤连接器的制定。乐泰eccobond F 123的债券提供的抗水和抗风化、气体、石油产品和其它有机和无机化合物。

固化材料的典型性能

触变指数1

粘度@ 25°C：

混合后的4000

比重，混合1.2

活性固体含量，% 100

锅寿命，小时4

闪点-见SDS

典型的固化性能

治疗计划

5分钟@ 100°C

替代治疗计划

2分钟@ 120°C或

1分钟@ 150°C

30分钟@ 150oC额外治愈后建议使用时温度高于150oC预计。

群众在0.25grams，让材料凝胶4小时@ 25oC跟着100oC 5小时

上述固化型材指南建议。